PENGARUH RASIO LIMBAH PLASTIK POLIPROPILENA (PP) DENGAN CAMPURAN SERBUK KAYU SENGON (Paraserianthes falcataria L.I.C. Nielsen) DAN SEKAM PADI (Oryza sativa) TERHADAP KUALITAS PAPAN KOMPOSIT PLASTIK
Abstract
The need for wood and plastic products is increasing, it is necessary to optimize the utilization of waste by processing it into plastic composite boards. This study aims to determine the best composition with raw materials of sengon wood powder (Paraserianthes falcataria L.I.C Nielsen) and rice husk powder (Oryza sativa) as filler with a ratio of 50% : 50% and polyprophylene plastic (PP) as a matrix. This treatment uses 3 compositions, P1 (40 % PP : 60 % SS) P2 (50% PP: 50% SS), and P3 (60% PP: 40 % SS ) was hot pressed with a pressure of 30 bar for 20 minutes at a temperature of 180°C with 3 replications for each treatment. The best result was obtained in the P3 (60 % PP : 40 % SS) with an average density value of 0.83 g/cm3, moisture content 1.52%, water absorption 32.16%, thickness swelling 9.34%, MoE 4,057.85 N/mm2, MoR 42.39 N/mm2 and IBS 0.21 N/mm2 Some test results have met plastic composite board standards according to JIS Particle Board A 5908-2003, JIS Plastic Board A 5741-2006 and SNI Plastic Board SNI 8154-2015.
Downloads
References
[2]Suseno, N. 2020. Dokumen Pemerintahan Desa Rekapan Sampah Tahunan Bank Sampah Desa Loa Duri Ilir. Tidak dipublikasikan
[3]BPS. 2021. Luas Panen dan Produksi Padi Di Indonesia.. Badan Pusat Statistik. Diunduh 4 Januari 2022. Tersedia pada : https://www.bps.go.id/publication/luas-panen-dan-produksi-padi-di-indonesia-2021.html.
[4]Kardiman., Fuadi, F.D.S., Faradina, C.S., Widyanto, E. 2019. Pengaruh Temperatur Terhadap Sifat Mekanik Pada Pembuatan Papan Komposit Berbasis Sekam Padi dan Matriks HDPE. Jurnal Ilmiah Teknik Mesin. 11(1) : 10-18
[5]Setyawati, D., Hadi, Y.S., Massijaya, M.Y., Nugroho, N. 2006. Kualitas Papan Komposit
[6]Akhsan, A. 2010. Variasi Waktu dan Suhu Kempa Terhadap Sifat Fisika dan Mekanika Papan komposit plastik Komposit Dari Serbuk Kayu Mahang (Macaranga gigantea Muell.Arg.) [Skripsi]. Fakultas Kehutanan Universitas Mulawarman. Samarinda.
[7]Pitria, I. 2010. Variasi Waktu Kempa dan Besar Tekanan Terhadap Sifat Fisika dan Mekanika Papan komposit plastik Komposit Dari Kayu Mahang (Macaranga gigantea Muell.Arg.) [Skripsi]. Fakultas Kehutanan Universitas Mulawarman. Samarinda.
[8]Andi, A., Setyawati, D., Nurhaida. 2021. Kualitas Papan Partikel Limbah Sekam Padi dan Limbah Finir Berdasarkan Susunan Lapisan Partikel Dan Kadar Perekat. Jurnal Hutan Lestari. 9(1) : 112-124.
[9]Wulandari, F.T. 2012. Deskripsi Sifat Fisika dan Mekanika Papan Partikel Tangkai Daun Nipah (Nypa fruticans Wurmb) dan Papan Partikel Batang Bengle (Zingiber cassumunar Roxb). Jurnal Media Ilmiah. 6(6) : 7-11.
[10]Fauziah., Wahyuni, D., Lapanporo, B.P. 2014. Analisis Sifat Fisika dan Mekanika Papan Partikel Berbahan Dasar Sekam Padi. Positron.4(2) : 60-63
[11]Fathanah, U. 2011. Kualitas Papan Komposit dari Sekam Padi dan Plastik HDPE Daur Ulang Menggunakan Maleic Anhydride (MAH) sebagai Compatibilizer. Jurnal Rekayasa Kimia dan Lingkungan.8(2) : 53-59
[12]Fithriani, D., Tri, N., Jamal, B. 2006. Pengaruh Waktu Pengempaan Terhadap Karakteristik Papan Partikel Dari Limbah Padat Pengolahan (Gracilaria sp). Jurnal Pascapanen dan Bioteknologi Kelautan dan Perikanan. 1(2):125-132.
[13]Astari, L., Nila, A.P., Gilang, D., Sudarmanto., Mohammad, G., Kurnia, W.P. 2018. Sifat Fisis-Mekanis dan Akustik Papan Partikel Berbahan Sabut Kelapa. Prosiding Seminar Lignoselulosa, Pusat Penelitian LIPI Bogor, Fakultas Kehutanan Universitas Muhammadiyah Sumatra Barat. Prosiding Seminar Lignoselulosa. Hal 155-160