PEMBUATAN MEMBRAN SILIKA DARI FLY ASH BATUBARA UNTUK PENURUNAN INTENSITAS WARNA DARI LIMBAH CAIR INDUSTRI SARUNG SAMARINDA
Abstract
Synthesis of silica membrane from coal fly ash to decrease the color intensity of the liquid waste of sarung Samarinda industry has been done. The extraction of silica from coal fly ash by using the sol-gel process, and for silica membrane by using mixture of PVA (Poly Viny Acohol) and PEG (Polyethylen Glycol. Decrease in color intensity were analyzed using UV-Visible Spectrofotometer and the morphology of the membrane was observed by SEM-EDX. Based on the results from the spectrofotometer the concentration of the liquid waste berofe is 52.92 Unit Pt.Co and after decolorization is 25.04 Unit Pt.Co. The result show that decreasing are concentration is 52.68%, and the results the Scanning Electron Microscope (SEM)-EDX on the membrane after decolorization of liquid waste show distribution of pores in the membrane experiencing changes caused by new particles covering membrane be expected from liquid waste, and the elements are C, O, Na, Al and Si.
Keyword
Coal Fly Ash, Liquid Waste of Sarung Samarinda, Membrane
Downloads
Download data is not yet available.
References
[1] Haspiadi. 2012. Penurunan Warna Limbah Cair Industri sarung samarinda dengan Karbon Aktif dari Batubara Kotor. Jurnal BARISTAND Vol. 6 No.11
[2] Effendi, H. 2003. Telaah Kualitas Air; Bagi Pengelolaan Sumber Daya dan Lingkungan Perairan. Yogyakarta: Kanisius.
[3] Rini, AP., Rum, H., Gunawan. 2009. Pengaruh Poly Ethilene Glycol (PEG) Dalam Sintesis Membran Padat Silika Dari Sekam Padi Dan Aplikasinya Untuk Dekolorisasi Limbah Cair Batik. Makalah Penelitian UNDIP: Semarang.
[4] Rachmawati, V dan Damayanti, A. 2013. Pengolahan Limbah Cair Industri Pewarnaan Jeans Menggunakan Membran Silika Nanofiltrasi Aliran Cross Flow Untuk Menurunkan Warna dan Kekeruhan, Jurusan Teknik Lingkungan, Jurnal Teknik Pomits, 2(2), 23-37.
[5] Suprihatin, E., Titin, A.Z dan Nelly, W. 2015. Pembuatan Membran Silika dari Fly Ash dan Aplikasinya Untuk Menurunkan Kadar COD dan BOD dari limbah Cair kelapa sawit. Volume 4(3) halaman 48-53.
[6] Rosnelly, C.M. 2010. Pengaruh Rasio Anhidrida Asetat dalam Proses Asetilasi Selulosa Pulp Kayu Sengon (Paraserianthes falcataria) dalam Pembuatan Polimer Selulosa Triasetat. Vol.27 No.1 Juni 2010, pp 1-11. Bogor: Teknologi Industri Pertanian-Fateta IPB.
[7] Setyawan, A., Musabbikhah., Retno. T.N dan Ainur, R. 2009. Rekayasa Unit Pengolah Limbah Batubara dan Pemanfaatannya sebagai Pengganti Semen pada Pembuatan Bahan Bangunan guna Mengendalikan Pencemaran Lingkungan. Jurnal Sains.
[8] Kalapathy, U., Proctor, A., Shults, J. 2000. A simple method for production of pure silica from ricehull ash. Bioresource Technology. 73. hlm 257-262.
[9] Mujiyanti, D.R., Nuryono dan Eko, S.K. 2016. Sintesis dan Karakterisasi Silika Gel Dari Abu Sekam Padi Yang Dimobilisasi Dengan 3-(Trimetoksilsill)-1Propantiol. Jurnal KIMIA, FMIPA, UNLAM dan UGM: KALSEL dan Yogyakarta.
[10] Astuti, M. D., Radna, N., Dwi, R.M. Imobilisasi1,8Dihidroxyanthraquinn Pada Silika Gel Melalui Proses Sol-Gel. Jurnal Jurusan Kimia, FMIPA UNLAM, KALSEL.
[11] Nazriati., Heru, S., Sugeng, W., Reza, A., Enggar E. V. 2011. Sintesis Silika Aerogel Dengan Bahan Dasar Abu Bagasse. Jurnal Teknik Kimia Vol. 13 No. 4 Hal 220-224, ITS: Surabaya.
[12] Meilina, N. 2010. Pengaruh Penambahan Merkaptobenzotiazol (MBT) Terhadap Kemampuan Adsropsi Silika Gel Dari Abu Bagasse Pada Ion Logam kadmium(II). Skripsi dari Jurusan KIMIA, FMIPA UNY: Yogyakarta.
[13] Uno, N.R., Sri, S dan Widya, A.L. 2015. Validasi Metode Analisis Untuk Penetapan Kadar Tablet Asam Mefenamat Secara Spektrofotometri Ultraviolet. Jurnal Ilmiah Farmasi Vo. 4 No 4, Manado: FMIPA UNSRAT.
[14] Jonathan, S. 2006. Metode Penelitian Kuantitatif dan Kualitatif. Yogyakarta: Graha Ilmu.
[15] Prameswari, T., Eko, B.S dan Agung, T.P. 2014. Sintesis Membran Kitosan-Silika Abu sekam padi Untuk Dekolorisasi Zat warna Congo Red. Jurnal Indo. J. Chem. Sci. 3(1)
[16] Febriyana, N.A., Zakiyatul.,M., Ach, A.,Wijayanto dan Novan, P. 2014. Analisis Jerami Padi Untuk Pembuatan Mikromembran Sebagai Pendaur Air Limbah Rumah Tangga. Jurnal Institut Teknologi Sepuluh November Surabaya.
[17] Aprilia, N.I., Sumarni, W dan Susatyo, E.B. 2012. Sintesis Membran Padat Silika Abu Sekam Padi dan Aplikasinya Untuk Penurunan Dekolorisasi Rhodamin B pada Limbah cair. Jurnal Sains no 1(2).
[2] Effendi, H. 2003. Telaah Kualitas Air; Bagi Pengelolaan Sumber Daya dan Lingkungan Perairan. Yogyakarta: Kanisius.
[3] Rini, AP., Rum, H., Gunawan. 2009. Pengaruh Poly Ethilene Glycol (PEG) Dalam Sintesis Membran Padat Silika Dari Sekam Padi Dan Aplikasinya Untuk Dekolorisasi Limbah Cair Batik. Makalah Penelitian UNDIP: Semarang.
[4] Rachmawati, V dan Damayanti, A. 2013. Pengolahan Limbah Cair Industri Pewarnaan Jeans Menggunakan Membran Silika Nanofiltrasi Aliran Cross Flow Untuk Menurunkan Warna dan Kekeruhan, Jurusan Teknik Lingkungan, Jurnal Teknik Pomits, 2(2), 23-37.
[5] Suprihatin, E., Titin, A.Z dan Nelly, W. 2015. Pembuatan Membran Silika dari Fly Ash dan Aplikasinya Untuk Menurunkan Kadar COD dan BOD dari limbah Cair kelapa sawit. Volume 4(3) halaman 48-53.
[6] Rosnelly, C.M. 2010. Pengaruh Rasio Anhidrida Asetat dalam Proses Asetilasi Selulosa Pulp Kayu Sengon (Paraserianthes falcataria) dalam Pembuatan Polimer Selulosa Triasetat. Vol.27 No.1 Juni 2010, pp 1-11. Bogor: Teknologi Industri Pertanian-Fateta IPB.
[7] Setyawan, A., Musabbikhah., Retno. T.N dan Ainur, R. 2009. Rekayasa Unit Pengolah Limbah Batubara dan Pemanfaatannya sebagai Pengganti Semen pada Pembuatan Bahan Bangunan guna Mengendalikan Pencemaran Lingkungan. Jurnal Sains.
[8] Kalapathy, U., Proctor, A., Shults, J. 2000. A simple method for production of pure silica from ricehull ash. Bioresource Technology. 73. hlm 257-262.
[9] Mujiyanti, D.R., Nuryono dan Eko, S.K. 2016. Sintesis dan Karakterisasi Silika Gel Dari Abu Sekam Padi Yang Dimobilisasi Dengan 3-(Trimetoksilsill)-1Propantiol. Jurnal KIMIA, FMIPA, UNLAM dan UGM: KALSEL dan Yogyakarta.
[10] Astuti, M. D., Radna, N., Dwi, R.M. Imobilisasi1,8Dihidroxyanthraquinn Pada Silika Gel Melalui Proses Sol-Gel. Jurnal Jurusan Kimia, FMIPA UNLAM, KALSEL.
[11] Nazriati., Heru, S., Sugeng, W., Reza, A., Enggar E. V. 2011. Sintesis Silika Aerogel Dengan Bahan Dasar Abu Bagasse. Jurnal Teknik Kimia Vol. 13 No. 4 Hal 220-224, ITS: Surabaya.
[12] Meilina, N. 2010. Pengaruh Penambahan Merkaptobenzotiazol (MBT) Terhadap Kemampuan Adsropsi Silika Gel Dari Abu Bagasse Pada Ion Logam kadmium(II). Skripsi dari Jurusan KIMIA, FMIPA UNY: Yogyakarta.
[13] Uno, N.R., Sri, S dan Widya, A.L. 2015. Validasi Metode Analisis Untuk Penetapan Kadar Tablet Asam Mefenamat Secara Spektrofotometri Ultraviolet. Jurnal Ilmiah Farmasi Vo. 4 No 4, Manado: FMIPA UNSRAT.
[14] Jonathan, S. 2006. Metode Penelitian Kuantitatif dan Kualitatif. Yogyakarta: Graha Ilmu.
[15] Prameswari, T., Eko, B.S dan Agung, T.P. 2014. Sintesis Membran Kitosan-Silika Abu sekam padi Untuk Dekolorisasi Zat warna Congo Red. Jurnal Indo. J. Chem. Sci. 3(1)
[16] Febriyana, N.A., Zakiyatul.,M., Ach, A.,Wijayanto dan Novan, P. 2014. Analisis Jerami Padi Untuk Pembuatan Mikromembran Sebagai Pendaur Air Limbah Rumah Tangga. Jurnal Institut Teknologi Sepuluh November Surabaya.
[17] Aprilia, N.I., Sumarni, W dan Susatyo, E.B. 2012. Sintesis Membran Padat Silika Abu Sekam Padi dan Aplikasinya Untuk Penurunan Dekolorisasi Rhodamin B pada Limbah cair. Jurnal Sains no 1(2).
Published
2018-03-28
How to Cite
PRATIWI, Kartika; -, Bohari; GUNAWAN, Rahmat.
PEMBUATAN MEMBRAN SILIKA DARI FLY ASH BATUBARA UNTUK PENURUNAN INTENSITAS WARNA DARI LIMBAH CAIR INDUSTRI SARUNG SAMARINDA.
JURNAL ATOMIK, [S.l.], v. 3, n. 1, p. 31-38, mar. 2018.
ISSN 2549-0052.
Available at: <http://jurnal.kimia.fmipa.unmul.ac.id/index.php/JA/article/view/614>. Date accessed: 20 apr. 2024.
Issue
Section
Artikel