MODIFIKASI KARBON AKTIF DARI CANGKANG JENGKOL DENGAN TiO2 UNTUK FOTODEGRADASI RHODAMIN B

  • Widya Rachmah Sari fmipa unmul
  • Noor Hindryawati Jurusan Kimia, Fakultas Matematika dan Ilmu Pengetahuan Alam, Universitas Mulawarman
  • R.R Dirgarini Julia Nurlianti Subagyono Jurusan Kimia, Fakultas Matematika dan Ilmu Pengetahuan Alam, Universitas Mulawarman

Abstract

Modifying activated carbon from jengkol shells with TiO2 to degrade Rhodamine by UV irradiation has been done. Modification of KA-TiO2 photocatalyst using the impregnation method. The photodegradation test of dyes was carried out with several parameters such as the variation of KA-TiO2 catalyst weight and contact time. Photocatalyst characterization using X-ray diffraction (XRD), while for dye concentration using UV-Vis spectrophotometry. Difractogram XRD shows that the activated carbon material after modification with TiO2 metal is characterized by the emergence of typical TiO2 peaks. The results showed that the highest percentage of Rhodamine B degraded by KA-TiO2 was 94.11% with a contact time of 120 minutes and a catalyst weight of 1.5 grams.


                                                                                                                                                


                                                                                                                                                 

Keyword
Activated carbon, TiO2, Dyestuffs, Photodegradation, UV

Downloads

Download data is not yet available.

References

[1] Cahyadi, W. 2008. Analisis & aspek kesehatan bahan tambahan pangan. Bumi aksara: Jakarta.
[2] Palupi, E. 2006. Degradasi Methylene Blue Dengan Metode Fotokatalisis dan Fotoelektrokatalisis Menggunakan Film TiO2. Skripsi, Jurusan Fisika, Fakultas MIPA, IPB, Bogor.
[3] Slamet, Ellyana, M., dan Bismo, S. 2006. Modifikasi zeolit alam lampung dengan fotokatalis tio2 melalui metode sol-gel dan aplikasinya untuk penyisihan fenol. Departemen Teknik Kimia, Fakultas Teknik, Universitas Indonesia..
[4] Joshi, A., & Shirivastva, J. 2010. Electrochemistry: Nanoelectrochemistry. Inggris: Royal Society of Chemistry Publishing.
[5] Tayade, R.,Kulkarni, Jasra. 2007. Enhanced photocatalytic activity of TiO2-Coated NaY and HY zeolites for the degradation of methylene blue in water. Ind. Eng. Chem. Res. 46:369-37.
[6] Hariati. 2017. Pembuatan Karbon Aktif dari Cangkang Jengkol (Pithecellobium lobatum) Melalui Bantuan Gelombang Ultrasonik Sebagai Bahan Penyimpan Energi Elektrokimia. Skripsi. Jurusan Kimia, Fakultas MIPA UNMUL.
[7] Riyani, K., dan Setyaningtyas, T. 2011. Pengaruh karbon aktif terhadap aktivitas fotodegradasi zat warna pada limbah cair industri tekstil menggunakan fotokatalis TiO2. FMIPA Kimia Universitas Jenderal Soedirman. 6(2), 113–122.
[8] Labanni. 2015. Sintesis dan karakteristik karbon nanopori ampas Tebu (Saccharum officianarum) dengan aktivator ZnCl2 melalui iradiasi ultrasonik sebagai bahan penyimpan energi elektrokimia. Jurnal: Jurusan Kimia. Universitas Hasanuddin. Makassar.
[9] Indramawan, R. 2016. Preparasi dan karakterisasi komposit CuO-zeolit alam untuk fotodegradasi zat warna Congo Red dengan sinar ultraviolet. Skripsi. Jurusan Kimia, Fakuktas MIPA, Universitas Negeri Yogyakarta.
[10] Rofiatun, N. 2013. Preparasi dan karakterisasi titanium dioksida dalam lingkungan basa kuat natrium hidroksida. Skripsi. Yogyakarta: Fakultas MIPA, Universitas Negeri Yogyakarta.
[11] Andari, D.N., dan Wardhani, S. 2014. Fotokatalis TiO2-Zeolit untuk degradasi metilen biru. Chem. Prog.
Published
2019-08-30
How to Cite
SARI, Widya Rachmah; HINDRYAWATI, Noor; SUBAGYONO, R.R Dirgarini Julia Nurlianti. MODIFIKASI KARBON AKTIF DARI CANGKANG JENGKOL DENGAN TiO2 UNTUK FOTODEGRADASI RHODAMIN B. JURNAL ATOMIK, [S.l.], v. 4, n. 2, p. 64-68, aug. 2019. ISSN 2549-0052. Available at: <http://jurnal.kimia.fmipa.unmul.ac.id/index.php/JA/article/view/744>. Date accessed: 27 sep. 2020.
Section
Artikel