STUDI VARIASI BERAT KATALIS DALAM FOTODEGRADASI RHODAMIN B MENGGUNAKAN KOMPOSIT WO3/TiO2/SiO2
Abstract
A study on photodegradation activity of Rhodamine B by WO3/TiO2/SiO2 composites in various material weight condition has been conducted. The photocatalytic process was carried out in a closed reactor equipped with visible lamps (grow LED 10 watt). To identify crystal structure, morphology and composition of composite WO3/TiO2/SiO2, the characterization performed using Scanning Electron Microscopy-Energy Diffraction-X (SEM-EDX). The results of characterization using SEM-EDX showed that composites have a non-uniform pore morphology. The photocatalytic test showed the optimum material weight at 0.15 gram with percent degradation of Rhodamine B dyes of 85.10%.
Downloads
Download data is not yet available.
References
[1] Yanyan L., Kurniawan T. A., Ying Z., Albadarin A. B., and Walker G. 2017. Enhanced photocatalytic degradation of acetaminophen from wastewater using WO3/TiO2/SiO2 composite under UV–VIS irradiation. Journal of Molecular Liquids. 243:761–70.
[2] Purnawan C, Patiha dan Qodri A. A. 2011. Fotodegradasi zat warna remazol yellow Fg dengan fotokatalis komposit TiO2/SiO2. Jurnal Ekosains. III(1).
[3] Syam B dan H. Widiyandari. 2014. Sintesis film tungsten oksida (WO3) dengan penambahan metal Co-katalis besi (Fe) dan aplikasinya pada peningkatan aktivitas fotokatalitik degradasi zat warna methylene blue menggunakan cahaya matahari. Youngster Physics Journal. 2(1):15-24.
[4] Hunge Y.M., M. A. Mahadik, A.V. Moholkar dan C. H. Bhosale. 2017. Photoelectrocatalytic degradation of oxalic acid using WO3 and stratified WO3/TiO2 photocatalysts under sunlight illumination. Journal Ultrasonics Sonochemistry. Volume 35, Part A, pages 233-242.
[5] Wardhani S dan Andari N. D. 2014. Fotokatalis TiO2-Zeolit untuk degradasi metilen biru. Jurnal Universitas Brawijaya Chem. Prg. 7(1).
[6] Basthomi, Ibnu A. 2016. Sintesis, karakterisasi dan uji aktivitas fotokatalis titanium dioksida (TiO2) anatas terdoping vanadium (III) menggunakan metode sonikasi. Skripsi. Malang: Universitas Islam Negeri Maulana Malik Ibrahim Malang.
[7] Sumartono A. dan Andayani W. 2007. The use of TiO2-zeolit as a catalyst on the degradation process of erionil red dye. Indo J. Chem. 7(1):141–46.
[2] Purnawan C, Patiha dan Qodri A. A. 2011. Fotodegradasi zat warna remazol yellow Fg dengan fotokatalis komposit TiO2/SiO2. Jurnal Ekosains. III(1).
[3] Syam B dan H. Widiyandari. 2014. Sintesis film tungsten oksida (WO3) dengan penambahan metal Co-katalis besi (Fe) dan aplikasinya pada peningkatan aktivitas fotokatalitik degradasi zat warna methylene blue menggunakan cahaya matahari. Youngster Physics Journal. 2(1):15-24.
[4] Hunge Y.M., M. A. Mahadik, A.V. Moholkar dan C. H. Bhosale. 2017. Photoelectrocatalytic degradation of oxalic acid using WO3 and stratified WO3/TiO2 photocatalysts under sunlight illumination. Journal Ultrasonics Sonochemistry. Volume 35, Part A, pages 233-242.
[5] Wardhani S dan Andari N. D. 2014. Fotokatalis TiO2-Zeolit untuk degradasi metilen biru. Jurnal Universitas Brawijaya Chem. Prg. 7(1).
[6] Basthomi, Ibnu A. 2016. Sintesis, karakterisasi dan uji aktivitas fotokatalis titanium dioksida (TiO2) anatas terdoping vanadium (III) menggunakan metode sonikasi. Skripsi. Malang: Universitas Islam Negeri Maulana Malik Ibrahim Malang.
[7] Sumartono A. dan Andayani W. 2007. The use of TiO2-zeolit as a catalyst on the degradation process of erionil red dye. Indo J. Chem. 7(1):141–46.
Published
2020-09-28
How to Cite
ADHAINA, Karina; HINDRYAWATI, Noor; KOESNARPADI, Soerja.
STUDI VARIASI BERAT KATALIS DALAM FOTODEGRADASI RHODAMIN B MENGGUNAKAN KOMPOSIT WO3/TiO2/SiO2.
JURNAL ATOMIK, [S.l.], v. 5, n. 1, p. 50-52, sep. 2020.
ISSN 2549-0052.
Available at: <http://jurnal.kimia.fmipa.unmul.ac.id/index.php/JA/article/view/943>. Date accessed: 26 apr. 2024.
Issue
Section
Artikel