MODIFIKASI DAN KARAKTERISASI ZEOLIT ALAM TASIKMALAYA DENGAN Fe2O3

  • Reka Oktaviani FMIPA UNMUL
  • Noor Hindryawati Jurusan Kimia, Fakultas Matematika dan Ilmu Pengetahuan Alam, Universitas Mulawarman
  • Aman Sentosa Panggabean Jurusan Kimia, Fakultas Matematika dan Ilmu Pengetahuan Alam, Universitas Mulawarman

Abstract

Research on natural zeolite has been carried out as a porous material modified by Fe2O3 semiconductor material. Starting with natural zeolite preparation, dealumination by activating it using HCl solution, modifying natural zeolite with Fe2O3 using FeCl3 and NaOH solution, then characterized using X-Ray Fluorescence (XRF), X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and test the surface area using a Methylene Blue solution. The results of the XRF analysis showed that the composition of Fe2O3 increased after it was modified to 38.022%, which was previously namely 3.193%. The results of SEM analysis showed changes in the morphology of natural zeolites after being modified with Fe2O3. The results of the XRD analysis showed that there was a diffraction peak which provided information that the sample contained Fe2O3. Zeolite-Fe2O3 has a surface area of ??110,2707 m2/g. 


Keywords : natural zeolite, Fe2O3, semiconduktor

Keyword
Natural Zeolite, Fe2O3, Semiconductor

Downloads

Download data is not yet available.

References

[1] Amelia, R. 2003. Pengaruh Konsentrasi Molekul Pengarah Terhadap Kristalinitas dan Komposisi Mineral Zeolit Pada Modifikasi Zeolit Alam Wonosari. Semarang: Universitas Diponegoro.
[2] Cromain, C. N dan Cahyaningrum, S.E. 2016. Karakterisasi Bentonit Terpilar Fe2O3 Sebagai Adsorben. UNESA Journal of Chemistry. Vol. 5 No 3.
[3] Dawy, M., Safaa, K dan Aziz. 2012. Synthesis, Characterization and Optical Properties of α- Fe2O3 Nanoparticle. Journal Basic Appl Sci. 6(4):55–62.ISSN 1991-8178.
[4] Dina, H. 2004. Pengaruh Perlakuan Beberapa Jenis Asam Terhadap Kemampuan Adsorpsi Cd (II) oleh Zeolit. Semarang: UNNES.
[5] Erawati, T., Rosita, N dan Retnosari. 2003. Penentuan Daya Serap Zeolit Alam Malang Selatan Terhadap Biru Metilen dan Kuinin HCl. Farmasi Airlangga. Vol.2 No.3.
[6] Fatimah, I dan Wijaya, K. 2005. Sintesis TiO2/Zeolit Sebagai Fotokatalis Pada Pengolahan Limbah Cair Industri Tapioka Secara Adsorpsi Fotodegradasi. TEKNOIN. Vol.10 No. 4:257-267.
[7] Handhoyo, R., Prijatama H., Sofiyah S., Nurlela I., Yusianita N., Amelia R dan Komala R. 2005. Peningkatan Rasio Si/Al Zeolit Alam Mordenit Sebagai Bahan Dasar Zeolit Katalis. Jurnal Indonesia. Bandung: Pusat Geoteknologi LIPI. Vol. 4 No 1.
[8] Heraldy E., Hisyam SW dan Sulistiyono. 2003. Karakterisasi dan Aktivasi Zeolit Alam Ponorogo. Surakarta: Jurusan Kimia FMIPA Universitas Sebelas Maret.
[9] Korkuna O., Leboda R., Skubiszewska J., Vrublevs T., Gun V.M., Ryczkowski J. 2006. Structural and Physicochemical Properties of Natural Zeolites, Clinoptilolite and Mordenite. Microporous and Mesoporous Mat. 87:243-254.
[10] Sumartono, A dan Andayani, W. 2007. The Use of TiO2-Zeolit as a Catalyston the Degradaton Process of Erionil Red Dye. Indonesian Journal of Chemistry. Vol. 7 No. 1:141-146.
Published
2019-12-09
How to Cite
OKTAVIANI, Reka; HINDRYAWATI, Noor; PANGGABEAN, Aman Sentosa. MODIFIKASI DAN KARAKTERISASI ZEOLIT ALAM TASIKMALAYA DENGAN Fe2O3. JURNAL ATOMIK, [S.l.], v. 4, n. 1, p. 30-35, dec. 2019. ISSN 2549-0052. Available at: <https://jurnal.kimia.fmipa.unmul.ac.id/index.php/JA/article/view/704>. Date accessed: 13 july 2024.
Section
Artikel